دانشگاه صنعتی اصفهان روشهای عددی در مهندسی 2228-7698 18 1 1999 04 15 Combustion Synthesis of Titanium-Tungsten Carbide Composites in Iron Matrix تولید کامپوزیت کاربید تنگستن-تیتانیم در زمینه آهن به روش سنتز احتراقی 171 180 2714 FA علی سعیدی و محمدعلی گلعذار Journal Article 2022 12 31 Combustion synthesis has been used to produce Fe-(Ti,W)C composites. A simple reactor was designed which made it possible to ignite the samples under controlled atmosphere. Samples with different W/Ti ratio were ingnited under argon atmosphere by an electric arc and a self-propagating reaction was initiated in each sample. Different composites such as WC in Fe-Ti matrix, WC+(Ti,W)C in Fe matrix, and (Ti, W)C in iron matrix were produced by changing W/Ti ratio in the starting materials. Examination of the microstructure revealed that WC had an angular morphology while (Ti, W)C particles were spherical. از روش سنتز احتراقی برای تولید کامپوزیت ذره ای Fe-(Ti,W)C استفاده شده است. راکتور ساده ای طراحی و ساخته شد که امکان انجام آزمایشها را تحت خلاء و آتمسفر خاص و شرایط کنترل پذیر از نظر دما و احتراق اولیه فراهم می سازد. نمونه هایی از مخلوط پودرهای آهن، تیتانیم، تنگستن و کربن با نسبتهای متفاوت از W/Ti تهیه شد و توسط جرقۀ الکتریکی تحت W/Ti در مخلوط اولیه کامپوزیتهای متفاوتی شامل WC در زمینۀ Fe-Ti، WC+(Ti,W)C در زمینۀ Fe و (Ti,W)C درر زمینۀ Fe تولید شد. فاز WC دارای ساختمان بلوری با مورفولوژی زاویه دار است ولی فاز (Ti,W)C مانند کاربید تیتانیم دارای مورفولوژی مدور است. https://jcme.iut.ac.ir/article_2714_b628386c9b92481fab68fbf284bd6a64.pdf