Isfahan University of Technology Journal of Computational Methods in Engineering 2228-7698 23 1 2022 12 31 Microstructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation Microstructural Evaluation of Ti-6AL-4V Alloy during Hot Deformation 189 201 2865 FA K. Farmanesh And A. Najafi-Zadeh Journal Article 2022 12 31 Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to different straining temperatures from 1050 to 850°C. The cooling rate was chosen fast enough to prevent high temperature transformation during cooling. A series of isothermal compression tests were conducted at different temperatures of 850, 900, 950, 1000, 1050°C at constant true strain rates of 0.1, 0.01 and 0.001 s-1, respectively. Samples were uniaxialy compressed to a true strain of 0.55 followed by water quenching to room temperature. The apparent activation energy for compression in two phase regions was calculated at 840 KJmol-1. The partial globularization of a-phase was observed in the specimens deformed at low strain rates and at temperatures near the transformation zone followed by annealing. Among the titanium alloys, Ti-6Al-4V is the most widely used. In the present work, the uniaxial hot compressive behavior of Ti-6Al-4V has been investigated under constant strain rates. A series of dilatometery experiments were carried out to determine the transformation temperatures at different cooling rates. Specimens were homogenized at 1050 °C for 10 minutes followed by fast cooling to different straining temperatures from 1050 to 850°C. The cooling rate was chosen fast enough to prevent high temperature transformation during cooling. A series of isothermal compression tests were conducted at different temperatures of 850, 900, 950, 1000, 1050°C at constant true strain rates of 0.1, 0.01 and 0.001 s-1, respectively. Samples were uniaxialy compressed to a true strain of 0.55 followed by water quenching to room temperature. The apparent activation energy for compression in two phase regions was calculated at 840 KJmol-1. The partial globularization of a-phase was observed in the specimens deformed at low strain rates and at temperatures near the transformation zone followed by annealing. https://jcme.iut.ac.ir/article_2865_85690f81aadc1749175c187784afc9ee.pdf